ISO 10477 pdf free download

ISO 10477-2020 pdf free download.Dentistry一Polymer-based crown and veneering materials.
5.5 Bond strength
5.5.1 Special bonding system without macromechanical retention
If the manufacturer recommends a special bonding system without macromechanical retention, the strength of bond to the material used for the substructure shall be not less than 5 MPa (see Tables 1 and 2).
Testing shall be carried out in accordance with Th.
5.5.2 Values higher than 5 MPa
lithe manufacturer claims a value higher than 5 MPa for the bond strength, then the bond strength shall be not less than 80 % of the value claimed.
Testing shall be carried out in accordance with 2.
5.6 Water sorption
The water sorption of the cured polymer-based crown and veneering material shall be not more than 40 Ig/mm3 (see Table 2).
Testing shall be carried out in accordance with 21. This requirement is not applicable to opaque resins.
5.7 Solubility
The solubility in water of the cured polymer-based crown and veneering material shall be not more than 7,5 ig/mm3 (see Table 2).
Testing shall be carried out in accordance with 71. This requirement is not applicable to opaque resins.
5.8 Shade consistency
The colours of the cured polymer-based crown and veneering material from different batches (according to ft.1 and 62) shall show no more than a slight difference with the colour indicated by the manufacturer.
Testing shall be carried out in accordance with 7, and ISO 7491. This requirement is not applicable to opaque resins.
5.9 Colour stability
The polymer-based crown and veneering material shall show no more than a slight change in colour.
Testing shall be carried out in accordance with 7 and ISO 7491. This requirement is not applicable to
opaque resins.
5.10 Biocompatibility
Refer to the Introduction for guidance on biocompatibility.
6 Sampling
6.1 For all tests
The test sample shall consist of one or more packages of one selected shade, corresponding to the purpose of the test, from a single batch and contain sufficient (approximately 20 ml) material to carry out the specified tests, plus an allowance for any necessary repetition of tests.
5.5 Bond strength
5.5.1 Special bonding system without macromechanical retention
If the manufacturer recommends a special bonding system without macromechanical retention, the strength of bond to the material used for the substructure shall be not less than 5 MPa (see Tables 1 and 2).
Testing shall be carried out in accordance with 7.6.
5.5.2 Values higher than 5 MPa
lithe manufacturer claims a value higher than 5 MPa for the bond strength, then the bond strength shall be not less than 80 % of the value claimed.
Testing shall be carried out in accordance with Z.6.
5.6 Water sorption
The water sorption of the cured polymer-based crown and veneering material shall be not more than 40 .tg/mm3 (see Table 2).
Testing shall be carried out in accordance with 71. This requirement is not applicable to opaque resins.
5.7 Solubility
The solubility in water of the cured polymer-based crown and veneering material shall be not more than 7,5 ig/mm3 (see Table 2).
Testing shall be carried out in accordance with 71. This requirement is not applicable to opaque resins.
5.8 Shade consistency
The colours of the cured polymer-based crown and veneering material from different batches (according to 61 and 62) shall show no more than a slight difference with the colour indicated by the manufacturer.
Testing shall be carried out in accordance with 7 and ISO 7491. This requirement is not applicable to opaque resins.ISO 10477 pdf download.