ISO 9647-2020 pdf free download.Steel – Determination of vanadium content – Flame atomic absorption spectrometric method (FAAS).
5 Reagents
During the analysis, unless otherwise specified, use only reagents of recognized analytical grade and
only grade 2 water as specified in ISO 3696.
5.1 Pure iron, containing <0,000 5 % of vanadium or of low and known vanadium content.
5.2 Hydrochloric acid, p approximately 1,19 g/ml.
5.3 Nitric acid, p approximately 1,40 g/ml.
5.4 Perchloric acid, p approximately 1,67 g/ml.
WARNING — Perchloric acid vapour can cause explosions in the presence of ammonia, nitrous fumes or organic material in general.
5.5 Hydrochloric acid solution, I + 50.
Add 10 ml of hydrochloric acid (5.2) to 500 ml of water and mix.
5.6 Aluminium solution, 20 g/l.
Dissolve 90 g of aluminium chloride hexahydrate (AICI3-6H20) in about 300 ml of water, add 5 ml of hydrochloric acid (52), dilute to 500 ml with water and mix.
5.7 Vanadium standard solution, 2,0 g/l.
5.7.1 Preparation using vanadium metal
Weigh (1,000 ± 0.001) g of vanadium (V  99.9 %) and transfer it into a 400 ml beaker. Add 30 ml of a mixture of three volumes of hydrochloric acid (52) and one volume of nitric acid (5.3).
Cover with a watch glass and if necessary heat gently to assist dissolution. When dissolution is complete evaporate the solution to just before dryness and add 20 ml of hydrochloric acid (52).
Allow to cool to room temperature and transfer the solution quantitatively into a 500 ml one-mark volumetric flask. Dilute to the mark with water and mix.
1 ml of this solution contains 2,0 mg of vanadium.
5.7.2 Preparation using ammonium metavanadate
Dry several grams of ammonium metavanadate (NH4VO3) (purity >99.9 %) in an oven at 100 °C to 105 °C for at least one hour and allow to cool to room temperature in a desiccator.
NOTE A drying temperature over 110 °C will cause decomposition of ammonium metavanadate. Keep strictly to the drying temperature specified.
Weight 2,296 g of the dried product into a 600 ml beaker, add about 400 ml of hot water and gently simmer to dissolve.
Allow to cool, transfer the solution quantitatively into a 500 ml one-mark volumetric flask. Dilute to the mark with water and mix.
1 ml of this solution contains 2,0 mg of vanadium.
2 © ISO 2020 — All rights reserved
Iso 9647:2020(E)
5.8 Vanadium standard solution, 0,08 g/l.
Transfer 10,0 ml of vanadium standard solution (51) into a 250 ml one-mark volumetric flask. Dilute to the mark with water and mix.
Prepare this solution immediately prior to use.
1 ml of this solution contains 0,08 mg of vanadium.
6 Apparatus
All volumetric glassware shall be class A, in accordance with ISO 648 or ISO 1042, as appropriate.
Ordinary laboratory apparatus and the following shall be used.
6.1 Atomic absorption spectrometer
The spectrometer shall be equipped with a vanadium hollow-cathode lamp and supplied with dinitrogen monoxide and acetylene sufficiently pure to give a steady clear fuel-lean flame, free from water and oil, and free from vanadium.
The atomic absorption spectrometer used will be satisfactory if, after optimization according to 8.3.3, the limit of detection and characteristic concentration are in reasonable agreement with the values given by the manufacturer and it meets the performance criteria given in 6J..J. to 61.3.
The instrument should also conform to the additional performance requirement given in 6J.A.
6.1.1 Minimum precision (see AnnexC)
The standard deviation of 10 measurements of the absorbance of the most concentrated calibration solution shall not exceed 1.0% of the mean absorbance of this solution.
The standard deviation of 10 measurements of the absorbance of the least concentrated calibration solution (excluding the zero member) shall not exceed 0,5 % of the mean absorbance of the most concentrated calibration solution.
6.1.2 Limit of detection (see AnnxC)
The limit of detection is a number, expressed in units of concentration (or amount) that describes the lowest concentration level (or amount) of an element that can be determined to be statistically different from an analytical blank.
The limit of detection of vanadium in a matrix similar to the final test solution shall be less than 0,3 pg/mI.
6.1.3 Calibration linearity (see Annex)
The slope of the calibration line covering the top 20 % of the concentration range (expressed as a change in absorbance) shall not be less than 0,7 times the value of the slope for the bottom 20 % of the concentration range determined in the same way.
For instruments with automatic calibration using two or more standard solutions, it shall be established prior to the analysis, by obtaining absorbance readings, that the above requirements for calibration linearity are fulfilled.
6.1.4 CharacterIstic concentration (see AnncxC)
The characteristic concentration for vanadium in a matrix similar to the final test solution shall be greater than 1 pg/mI.ISO 9647 pdf download.